Evaluation of the critical stress of anodized coating-AZ91D substrate using SEM in-situ technology
Abstract: Experimental investigations of the micro cracking behavior of a coating-substrate structure were carried out in-situ with a scanning electron microscope (SEM). An anodized coating layer was deposited on an AZ91D substrate by the galvanize pulse method. Results indicated that the failure mechanism of the coating-substrate structure was due to a mismatch of micro deformation between the coating and substrate. The micro deformations induced by different failure models were cracking, spalling, or delamination. The failure models were validated using theoretical, experimental, and digital image correlation methods. The critical stress of failure can be evaluated by measuring the biaxial stress.
Key words: Magnesium alloy, Anodized coating, Material mechanics, Flexural stress, Cracking behavior
创新点：在Stoney方程基础上首次用试验方法定量地表征氧化涂层与镁铝合金基体材料的弯曲失效应力值；建立梁或板最大弯曲扰度与临界失效应力之间的关系，弥补Stoney方程中没有考虑二维效应及涂层材料特性引起的不足，使之更加适合工程中常见涂层-基体结构的损伤特点。
方法：将如图1所示的涂层-基体结构试件断面仔细抛光后置于扫描电镜的真空腔内；边加载边观察断面中损伤行为的变化，特别是界面附近的变形和开裂状态；比较所对应的加载点位移和载荷大小，并把其作为评价损伤行为的力学 参数。
结论：本试验方法定量表征的涂层-基体结构临界弯曲失效应力值和失效位置与扫描电镜损伤演化图形的数字散斑分析结果一致，适合二维涂层-基体结构损伤应力的评价。
关键词组：
References:
Open peer comments: Debate/Discuss/Question/Opinion
<1>
DOI:
10.1631/jzus.A1500178
CLC number:
O343.1; O346.1; O348.3
Download Full Text:
Downloaded:
2812
Download summary:
<Click Here>Downloaded:
1991Clicked:
3850
Cited:
0
On-line Access:
2016-01-06
Received:
2015-06-13
Revision Accepted:
2015-11-09
Crosschecked:
2015-12-16