Abstract: To determine the ash characteristics during fluidized bed combustion and gasification purposes, the investigation of the impacts of chemical composition of Jincheng coal ash on the sintering temperature was conducted. A series of experiments on the sintering behavior at 0.5 MPa was performed using the pressurized pressure-drop technique in the combustion and gasification atmospheres. Meanwhile, the mineral transformations of sintered ash pellets were observed using X-ray diffractometer (XRD) analyzer to better understand the experimental results. In addition, quantitative XRD and field emission scanning electron microscope/energy dispersive X-ray spectrometer (FE-SEM/EDS) analyses of ash samples were used for clarifying the detailed ash melting mechanism. These results show that the addition of Fe₂O₃ can obviously reduce the sintering temperatures under gasification atmospheres, and only affect a little the sintering temperature under combustion atmosphere. This may be due to the presence of iron-bearing minerals, which will react with other ash compositions to produce low-melting-point eutectics. The FE-SEM/EDS analyses of ash samples with Fe₂O₃ additive show consistent results with the XRD measurements. The CaO and Na₂O can reduce the sintering temperatures under both the combustion and gasification atmospheres. This can be also contributed to the formation of low-melting-point eutectics, decreasing the sintering temperature. Moreover, the fluxing minerals, such as magnetite, anhydrite, muscovite, albite and nepheline, contribute mostly to the reduction of the sintering temperature while the feldspar minerals, such as anorthite, gehlenite and sanidine, can react with other minerals to produce low-melting-point eutectics, and thereby reduce the sintering temperatures.

Key words: Ash composition, Sintering temperature, X-ray diffractometer (XRD), Field emission scanning electron microscope/ energy dispersive X-ray spectrometer (FE-SEM/EDS)

Please provide your name, email address and a comment

Your Name: Affili: E-Mail Address:

Comment (Please comment in English):


Verification Code(click to change a pic):