Abstract: aluminum nitride (AlN) thin films with high c-axis orientation have been prepared on a glass substrate with an Al bottom electrode by radio frequency (RF) reactive magnetron sputtering. Based on the analysis of Berg’s hysteresis model, the improved sputtering system is realized without a hysteresis effect. A new control method for rapidly depositing highly c-axis oriented AlN thin films is proposed. The N₂ concentration could be controlled by observing the changes in cathode voltage, to realize the optimum processing condition where the target could be fixed stably in the transition region, and both stoichiometric film composition and a high deposition rate could be obtained. Under a 500 W RF power of a target with a 6 cm diameter, a substrate temperature of 450 °C, a target-substrate distance of 60 mm and a N₂ concentration of 25%, AlN thin film with preferential (002) orientation was deposited at 2.3 μm/h which is a much higher rate than previously achieved. Through X-ray diffraction (XRD) analysis, the full width at half maximum (FWHM) of AlN (002) was shown to be about 0.28°, which shows the good crystallinity and crystal orientation of AlN thin film. With other parameters held constant, any increase or decrease in N₂ concentration results in an increase in the FWHM of AlN.

[1] Berg, S., Nyberg, T., 2005. Fundamental understanding and modeling of reactive sputtering processes. Thin Solid Films, 476(2):215-230.

[2] Chiu, K.H., Chen, J.H., Chen, H.R., Huang, R.S., 2007. Deposition and characterization of reactive magnetron sputtered aluminum nitride thin films for film bulk acoustic wave resonator. Thin Solid Films, 515(11):4819-4825.

[3] Huang, C.L., Tay, K.W., Wu, L., 2005. Aluminum nitride films deposited under various sputtering parameters on molybdenum electrodes. Solid-State Electronics, 49(2):219-225.

[4] Lakin, K.M., 2003. A review of thin-film resonator technology. IEEE Microwave Magazine, 4(4):61-67.

[5] Mansurov, V.G., Nikitin, A.Y., Galitsyn, Y.G., Svitasheva, S.N., Zhuravlev, K.S., Osvath, Z., Dobos, L., Horvath, Z.E., Pecz, B., 2007. AlN growth on sapphire substrate by ammonia MBE. Journal of Crystal Growth, 300(1):145-150.

[6] Medjani, F., Sanjin, R., Allidi, G., Karimi, A., 2006. Effect of substrate temperature and bias voltage on the crystallite orientation in RF magnetron sputtered AlN thin films. Thin Solid Films, 515(1):260-265.

[7] Okano, H., Takahashi, Y., Tanaka, T., Shibata, K., Nakano, S., 1992. Preparation of c-axis oriented AlN thin films by low-temperature reactive sputtering. Japanese Journal of Applied Physics, 31:3446-3451.

[8] Ristoscu, C., Ducu, C., Socol, G., Craciunoiu, F., Mihailescu, I.N., 2005. Structural and optical characterization of AlN films grown by pulsed laser deposition. Applied Surface Science, 248(1-4):411-415.

[9] Ruby, R., Bradley, P., Larson, J.D.III, Oshmyansky, Y., 1999. PCS 1900 MHz duplexer using thin film bulk acoustic resonators (FBARs). Electronics Letters, 35(10):794-795.

[10] Sproul, W. D., Christie, D. J., Carter, D. C., 2005. Control of reactive sputtering processes. Thin Solid Films, 491(1-2):1-17.

[11] Tai, C.H., Shing, T.K., Lee, Y.D., Tien, C.C., 2004. A novel thin film bulk acoustic resonator (FBAR) duplexer for wireless applications. Tamkang Journal of Science and Engineering, 7(2):67-71.

[12] Weigel, R., Rappel, C., 2005. FBAR Filters for Cellular Phone Applications. 2005 IEEE MTT-S International, International Microwave Symposium Digest, p.207-208.

[13] Yang, C.M., Uehara, K., Kim, S.K., Kameda, S., Nakase,H., Tsubouchi, K., 2003. Highly c-axis-oriented AlN Film Using MOCVD for 5 GHz-band FBAR Filter. 2003 IEEE Ultrasonics Symposium, p.170-173.

[14] Yu, Y., Zhao, H.J., Gao, Z.Y., Ren, T.L., Liu, L.T., 2005. Deposition of AlN thin films on silicon by DC magnetron reactive sputtering. Piezoelectrics and Acoustooptics, 27(1):53-55 (in Chinese).