Abstract: silicon carbide (SiC) ceramic with YAG (Y₃Al₅O₁₂) additive added by sol-gel method was liquid-phase sintered at different sintering temperatures, and the sintering mechanism and microstructural characteristics of resulting silicon carbide ceramics were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and elemental distribution of surface (EDS). YAG (yttrium aluminum garnet) phase formed before the sintering and its uniform distribution in the SiC/YAG composite powder decreased the sintering temperature and improved the densification of SiC ceramic. The suitable sintering temperature was 1860 °C with the specimen sintered at this temperature having superior sintering and mechanical properties, smaller crystal size and fewer microstructure defects. Three characteristics of improved toughness of SiC ceramic with YAG added by sol-gel method were microstructural densification, main-crack deflection and crystal ‘bridging’.

[1] Biswas, K., Rixecker, G., 2001. Liquid phase sintering and microstructure-property relationships of silicon carbide ceramics with oxynitride additives. Materials Chemistry and Physics, 67:180-191.

[2] Brook, J.R., 1999. Processing of Ceramics Part II. Science Press of China, Beijing, p.88-105 (in Chinese).

[3] Huang, Z.H., Jia, D.C., 2003. A new sintering additive for silicon carbide ceramic. Ceramics International, 29:13-17.

[4] Izhevsikyi, V.A., Genova, L.A., 2001. Microstructure and properties tailoring of liquid-phase sintered SiC. International Journal of Refractory Metal & Hard Materials, 19:409-407.

[5] Jensen, R.P., Luecke, E.W., 2000. High-temperature properties of liquid-phase-sintered α-SiC. Materials Science and Engineering A, 282:109-114.

[6] Kim, Y.W., Kim, J.Y., 2000. Effect of initerial particle size on microstructure of liquid-phase sintered α-silicon carbide. Journal of the European Ceramic Society, 20:945-949.

[7] Lee, Y., Kim, Y.W., 2003. Fabrication of dense nanostructured silicon carbide ceramics through two-step sintering. Journal of American Ceramic Society, 86(10):1803-1805.

[8] Liden, E., Carlstrom, E., 1995. Homogeneous distribution of sintering additives in liquid-Phase sintered silicon carbide. Journal of the American Ceramic Society, 78(7):1761-1768.

[9] Samanta, A.K., Dhargupta, K.K., 2001. Decomposition reactions in the SiC-Al-Y-O system during gas pressure sintering. Ceramics International, 27:123-133.

[10] She, J.H., Ueno, K., 1999a. Effect of additive content on liquid-phase sintering on silicon carbide ceramics. Materials Research Bulletin, 34(10/11):1629-1636.

[11] She, J.H., Ueno, K., 1999b. Densification behavior and mechanical properties of pressureless-sintered silicon carbide ceramics with alumina and yttria additions. Materials Chemistry and Physics, 59:139-142.

[12] van Dijen, F.K., Mayer, E., 1996. Liquid phase sintering of silicon carbide. Journal of the European Ceramic Society, 16:413-420.

[13] Ye, H., Pujar, V.V., 1999. Coasening in liquid-phase-sintered α-SiC. Acta mater., 47(2):481-487.

[14] Zhang, L., Ru, H.Q., 2002. Sintering behavior and mechanical properties of the powder mixtures of SiC/YAG ceramics. Journal of Northeastern University (Natural Science), 23(7):667-670 (in Chinese).

[15] Zhou, Y., Hirao, K., 2003. Fracture-mode change in alumina-silicon carbide composites doped with rare-earth impurities. Journal of the European Ceramic Society, 24:265-270.